- 熔體流動速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in3 | |
| Thickness | 40.0 microns | 1.57 mil | |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg | 0.80 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.4 MPa | 1650 psi | |
| Film Tensile Strength at Yield, TD | 11.4 MPa | 1650 psi | |
| Film Elongation at Break, MD | 230 % | 230 % | |
| Film Elongation at Break, TD | 570 % | 570 % | |
| Coefficient of Friction | 0.30 | 0.30 | |
| Elmendorf Tear Strength MD | 420 g | 420 g | |
| Elmendorf Tear Strength TD | 170 g | 170 g | |
| Elmendorf Tear Strength, MD | 10.5 g/micron | 267 g/mil | |
| Elmendorf Tear Strength, TD | 4.30 g/micron | 109 g/mil | |
| Dart Drop | 3.30 g/micron | 83.8 g/mil | |
| Film Tensile Strength at Break, MD | 24.2 MPa | 3510 psi | |
| Film Tensile Strength at Break, TD | 20.3 MPa | 2940 psi | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 204 °C | 399 °F | Film extrusion temperature |