- 熔體流動速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in3 | ISO 1872/1 |
| Thickness | 15.0 microns | 0.591 mil | |
| Melt Flow | 0.90 g/10 min @Load 2.16 kg | 0.90 g/10 min @Load 4.76 lb | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ISO 1184 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ISO 1184 |
| Film Elongation at Break, MD | 620 % | 620 % | ISO 1184 |
| Film Elongation at Break, TD | 840 % | 840 % | ISO 1184 |
| Elmendorf Tear Strength, MD | 5.71 g/micron | 145 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 14.6 g/micron | 370 g/mil | ASTM D1922 |
| Dart Drop | 10.0 g/micron | 254 g/mil | Calculated from thickness |
| Dart drop Test | 150 g | 0.331 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 41.0 MPa | 5950 psi | ISO 1184 |
| Film Tensile Strength at Break, TD | 32.0 MPa | 4640 psi | ISO 1184 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 225 °C | 437 °F | |