- 熔體流動速率 [g/10min]: 50.0
- 密度 [g/cm3]: 0.926
- 缺口沖擊強度: 5.0
- 拉伸強度 [MPa]: 10.0
- 彎曲模量 [MPa]: 0.200
- 脆化溫度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in3 | load density; ASTM D1505 |
| ESCR 100% Igepal? | 6.0 hour | 6.0 hour | F50; ASTM D1693B |
| ESCR 10% Igepal? | 3.0 hour | 3.0 hour | F50; ASTM D1693B |
| Melt Flow | 50 g/10 min @Load 2.16 kg, Temperature 190 °C | 50 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 50 | 50 | ASTM D2240 |
| Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM D638 |
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | ASTM D638 |
| Elongation at Break | >= 350 % | >= 350 % | ASTM D638 |
| Flexural Strength | 8.00 MPa | 1160 psi | ASTM D790 |
| Flexural Modulus | 0.200 GPa | 29.0 ksi | ASTM D790 |
| 1% Secant Modulus | 240 MPa | 34800 psi | ASTM D638 |
| Izod Impact, Notched | 5.00 J/cm | 9.37 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 88.0 °C | 190 °F | ASTM D1525 |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 15.0 - 60.0 °C | 59.0 - 140 °F | |
| Injection Pressure | 60.0 - 100 MPa | 8700 - 14500 psi | |