- 熔體流動速率 [g/10min]: 2.8
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in3 | load density; ASTM D1505 |
| Thickness | 30.0 microns | 1.18 mil | |
| Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 13.0 MPa | 1890 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Elongation at Break, MD | 470 % | 470 % | ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 |
| Elmendorf Tear Strength MD | 65 g | 65 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 300 g | 300 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 2.17 g/micron | 55.1 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 10.0 g/micron | 254 g/mil | ASTM D1922 |
| Dart drop Total Energy | 570 J/cm | 1.07 ft-lb/mil | Puncture Resistance; SABIC Method |
| Dart Drop | 2.50 g/micron | 63.5 g/mil | ASTM D1709 |
| Dart drop Test | 75.0 g | 0.165 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 28.0 MPa | 4060 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 18.0 MPa | 2610 psi | ASTM D882 |
| 1% Secant Modulus, MD | 135 MPa | 19600 psi | ASTM D882 |
| 1% Secant Modulus, TD | 140 MPa | 20300 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 98.0 °C | 208 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 5.0 % | 5.0 % | ASTM D1003 |
| Gloss | 90 % | 90 % | at 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 250 - 300 °C | 482 - 572 °F | |
| Roll Temperature | 20.0 °C | 68.0 °F | |