- 熔體流動速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.915
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.915 g/cc | 0.0331 lb/in3 | ASTM D1505 |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.70 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 |
| Antiblock Level | 7000 ppm | 7000 ppm | |
| Slip Level | 1500 ppm | 1500 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.51 MPa | 1525 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.5 MPa | 1530 psi | ASTM D882 |
| Film Elongation at Break, MD | 670 % | 670 % | ASTM D882 |
| Film Elongation at Break, TD | 880 % | 880 % | ASTM D882 |
| Elmendorf Tear Strength MD | 465 g | 465 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 650 g | 650 g | ASTM D1922 |
| Dart drop Test | 535 g | 1.18 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 39.3 MPa | 5700 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 34.5 MPa | 5000 psi | ASTM D882 |
| Processing Properties | Metric | English | Comments |
| Blow-up Ratio (BUR) | 2.5 | 2.5 | |