- 熔體流動(dòng)速率 [g/10min]: 5.5
- 密度 [g/cm3]: 0.936
- 拉伸強(qiáng)度 [MPa]: 16.03
- 彎曲模量 [MPa]: 0.703
- 熱變形溫度 [℃]: 59.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in3 | ASTM D4883 | ||
| ESCR 100% Igepal? | 36 hour | 36 hour | ASTM D1693 | ||
| ESCR 10% Igepal? | 24 hour | 24 hour | ASTM D1693 | ||
| Melt Flow | 5.5 g/10 min | 5.5 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 16.03 MPa | 2325 psi | ASTM D638 | ||
| Elongation at Yield | 17.1 % | 17.1 % | ASTM D638 | ||
| Flexural Modulus | 0.703 GPa | 102 ksi | 1% secant; ASTM D790 | ||
| Impact Test | 70.5 J @Thickness 3.17 mm, Temperature -40.0 °C | 52.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | ARM | ||
| 156 J @Thickness 6.35 mm, Temperature -40.0 °C | 115 ft-lb @Thickness 0.250 in, Temperature -40.0 °F | ARM | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 125 °C | 257 °F | ASTM D3418 | ||
| Crystallization Temperature | 109.4 °C | 228.9 °F | ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 59.0 °C | 138 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 38.0 °C | 100 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Features | medium term UV 4 stabilization | ||||
| Form | PELLET | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.