- 熔體流動速率 [g/10min]: 6.8
- 密度 [g/cm3]: 0.936
- 拉伸強度 [MPa]: 17.2
- 彎曲模量 [MPa]: 0.689
- 熱變形溫度 [℃]: 59.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in3 | ASTM D4883 | ||
| ESCR 100% Igepal? | 300 hour | 300 hour | ASTM D1693 | ||
| ESCR 10% Igepal? | 60 hour | 60 hour | ASTM D1693 | ||
| Melt Flow | 6.8 g/10 min | 6.8 g/10 min | 190°C/2.16 kg; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 17.2 MPa | 2500 psi | 2.0 in/min; ASTM D638 | ||
| Elongation at Yield | 20 % | 20 % | 2.0 in/min; ASTM D638 | ||
| Flexural Modulus | 0.689 GPa | 100 ksi | 1% secant; ASTM D790 | ||
| Impact Test | 81.3 J @Thickness 3.17 mm, Temperature -40.0 °C | 60.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | ARM | ||
| 217 J @Thickness 6.35 mm, Temperature -40.0 °C | 160 ft-lb @Thickness 0.250 in, Temperature -40.0 °F | ARM | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 126 °C | 259 °F | ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 59.0 °C | 138 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 38.0 °C | 100 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Features | long term UV 8 stabilization | ||||
| Form | 35 US Mesh Powder | ||||