- 熔體流動速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.924
- 拉伸強度 [MPa]: 14.5
- 熱變形溫度 [℃]: 45.0
- 脆化溫度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in3 | ASTM D1505 |
| Melt Flow | 20.0 g/10 min | 20.0 g/10 min | ASTM D1238 |
| Spiral Flow | 32.0 cm | 12.6 in | Equistar |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 57.0 | 57.0 | ASTM D2240 |
| Tensile Strength at Break | 8.27 MPa | 1200 psi | 20 in/min; ASTM D638 |
| Tensile Strength, Yield | 14.5 MPa | 2100 psi | 20 in/min; ASTM D638 |
| Elongation at Yield | 12.0 % | 12.0 % | 20 in/min; ASTM D638 |
| 1% Secant Modulus | 434 MPa | 63000 psi | 0.5 in/min; ASTM D790 |
| 2% Secant Modulus | 0.379 GPa | 55.0 ksi | 0.5 in/min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | ASTM D648 |
| Vicat Softening Point | 91.1 °C | 196 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | F50; ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 177 °C | 350 °F | |
| Middle Barrel Temperature | 191 °C | 375 °F | |
| Front Barrel Temperature | 204 °C | 400 °F | |
| Nozzle Temperature | 204 °C | 400 °F | |
| Compliance Properties | Metric | English | Comments |
| FDA | Yes | Yes | |