- 熔體流動速率 [g/10min]: 0.85
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in3 | |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 0.85 g/10 min @Load 2.16 kg | 0.85 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 8. |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | |
| Secant Modulus, MD | 0.180 GPa | 26.1 ksi | Film value |
| Secant Modulus, TD | 0.185 GPa | 26.8 ksi | Film value |
| Elmendorf Tear Strength MD | 275 g | 275 g | |
| Elmendorf Tear Strength TD | 635 g | 635 g | |
| Elmendorf Tear Strength, MD | 11.0 g/micron | 279 g/mil | |
| Elmendorf Tear Strength, TD | 25.4 g/micron | 645 g/mil | |
| Dart Drop | 16.7 g/micron | 424 g/mil | |
| Film Tensile Strength at Break, MD | 52.0 MPa | 7540 psi | |
| Film Tensile Strength at Break, TD | 42.0 MPa | 6090 psi | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 98.0 °C | 208 °F | |
| Optical Properties | Metric | English | Comments |
| Haze | 6.0 % | 6.0 % | |
| Gloss | 65 % | 65 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 226 °C | 439 °F | Film extrusion temperature |