- 熔體流動速率 [g/10min]: 2.5
- 密度 [g/cm3]: 0.935
- 拉伸強度 [MPa]: 20.0
- 彎曲強度 [MPa]: 18.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in3 | |
| Thickness | 30.0 microns | 1.18 mil | |
| Melt Flow | 2.5 g/10 min @Load 2.16 kg | 2.5 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 7.2. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 18.3 MPa | 2650 psi | Molded property |
| Film Tensile Strength at Yield, MD | 15.2 MPa | 2200 psi | |
| Film Tensile Strength at Yield, TD | 18.6 MPa | 2700 psi | |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | Molded property |
| Film Elongation at Break, MD | 420 % | 420 % | |
| Film Elongation at Break, TD | 460 % | 460 % | |
| Elongation at Break | 400 % | 400 % | Molded value |
| Elmendorf Tear Strength MD | 70 g | 70 g | |
| Elmendorf Tear Strength TD | 470 g | 470 g | |
| Elmendorf Tear Strength, MD | 2.30 g/micron | 58.4 g/mil | |
| Elmendorf Tear Strength, TD | 15.7 g/micron | 399 g/mil | |
| Dart Drop | 1.70 g/micron | 43.2 g/mil | |
| Film Tensile Strength at Break, MD | 35.2 MPa | 5110 psi | |
| Film Tensile Strength at Break, TD | 31.0 MPa | 4500 psi | |
| Optical Properties | Metric | English | Comments |
| Haze | 3.5 % | 3.5 % | |
| Gloss | 85 % | 85 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 274 °C | 525 °F | Film extrusion temperature |