- 熔體流動(dòng)速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.926
- 拉伸強(qiáng)度 [MPa]: 15.1
- 彎曲強(qiáng)度 [MPa]: 24.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in3 | |
| Thickness | 40.0 microns | 1.57 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg | 1.0 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 8. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 24.8 MPa | 3600 psi | Molded property |
| Film Tensile Strength at Yield, MD | 12.7 MPa | 1840 psi | |
| Film Tensile Strength at Yield, TD | 15.1 MPa | 2190 psi | |
| Tensile Strength, Yield | 15.1 MPa | 2190 psi | Molded property |
| Film Elongation at Break, MD | 670 % | 670 % | |
| Film Elongation at Break, TD | 780 % | 780 % | |
| Elongation at Break | 850 % | 850 % | Molded value |
| Modulus of Elasticity | 0.330 GPa | 47.9 ksi | Molded Sample 2% Secant Modulus |
| Coefficient of Friction | 0.60 | 0.60 | |
| Elmendorf Tear Strength MD | 240 g | 240 g | |
| Elmendorf Tear Strength TD | 730 g | 730 g | |
| Elmendorf Tear Strength, MD | 6.00 g/micron | 152 g/mil | |
| Elmendorf Tear Strength, TD | 18.3 g/micron | 465 g/mil | |
| Dart Drop | 5.50 g/micron | 140 g/mil | |
| Film Tensile Strength at Break, MD | 39.6 MPa | 5740 psi | |
| Film Tensile Strength at Break, TD | 34.1 MPa | 4950 psi | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 106 °C | 223 °F | |
| Optical Properties | Metric | English | Comments |
| Haze | 15 % | 15 % | |
| Gloss | 45 % | 45 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 232 °C | 450 °F | Film extrusion temperature |