- 熔體流動速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in3 | ASTM D1505 |
| Melt Flow | 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.90 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 27.6 MPa @Thickness 0.0254 mm | 4000 psi @Thickness 0.00100 in | Transverse to Flow; ASTM D882 |
| 34.4 MPa @Thickness 0.0254 mm | 4990 psi @Thickness 0.00100 in | Direction of Flow; ASTM D882 | |
| Elongation at Break | 550 % @Thickness 0.0254 mm | 550 % @Thickness 0.00100 in | Direction of Flow; ASTM D882 |
| 600 % @Thickness 0.0254 mm | 600 % @Thickness 0.00100 in | Transverse to Flow; ASTM D882 | |
| Dart Drop, Total Energy | 140 J | 103 ft-lb | F50; ASTM D1709 |
| Tear Strength Test | 400 | 400 | g; Direction of Flow; ASTM D1922 |
| 750 | 750 | g; Transverse to Flow; ASTM D1922 | |
| Optical Properties | Metric | English | Comments |
| Haze | 20 % | 20 % | ASTM D1003 |
| Gloss | 50 % | 50 % | 45°; ASTM D2457 |