- 拉伸強度 [MPa]: 11.0
- 彎曲模量 [MPa]: 0.276
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.922 g/cc | 0.922 g/cc | ASTM D792 |
| Melt Index of Compound | 0.30 g/10 min | 0.30 g/10 min | Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | transverse direction; ASTM D882 |
| 13.8 MPa | 2000 psi | machine direction; ASTM D882 | |
| Elongation at Break | 400 % | 400 % | machine direction; ASTM D882 |
| 500 % | 500 % | transverse direction; ASTM D882 | |
| Flexural Modulus | 0.276 GPa | 40.0 ksi | 1% secant - machine direction; ASTM D882 |
| 0.310 GPa | 45.0 ksi | 1% secant - transverse direction; ASTM D882 | |
| Optical Properties | Metric | English | Comments |
| Gloss | 55 % | 55 % | ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 125 °C | 257 °F | |