- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.912
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.912 g/cc | 0.0329 lb/in3 | ASTM D1505 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 23.0 MPa | 3340 psi | ASTM D638 |
| Elongation at Break | 810 % | 810 % | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 124 °C | 255 °F | D.S.C. method |
| Vicat Softening Point | 88.0 °C | 190 °F | ASTM D1525-82 |
| Optical Properties | Metric | English | Comments |
| Haze | 5.5 % | 5.5 % | 50 microns film |