- 密度 [g/cm3]: 1.34
- 缺口沖擊強度: 3.5
- 彎曲模量 [MPa]: 2.40
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in3 | ISO 1183-87 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ISO DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | ISO 527-93 |
| Elongation at Break | 600 % | 600 % | ISO 527-93 |
| Flexural Strength | 70.0 MPa | 10200 psi | ISO 178-93 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 3.50 kJ/m2 | 1.67 ft-lb/in2 | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 245 °C | 473 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75-93 |