- 密度 [g/cm3]: 1.6
- 缺口沖擊強(qiáng)度: 0.69
- 斷裂伸長(zhǎng)率 [%]: 150
- 彎曲強(qiáng)度 [MPa]: 115.0
- 彎曲模量 [MPa]: 10.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in3 | ISO 1183-87 |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0090 cm/cm | 0.0060 - 0.0090 in/in | DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 115 MPa | 16700 psi | ISO 527-93 |
| Elongation at Break | 1.7 % | 1.7 % | ISO 527-93 |
| Flexural Yield Strength | 150 MPa | 21800 psi | ISO 178-93 |
| Flexural Modulus | 10.6 GPa | 1540 ksi | ISO 178-93 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 250 °C | 482 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-93 |