- 熔體流動速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.5
- 缺口沖擊強度: 4.27
- 拉伸強度 [MPa]: 47.0
- 斷裂伸長率 [%]: 71.0
- 彎曲模量 [MPa]: 1.86
- 熱變形溫度 [℃]: 114.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D 792 |
| Density | 1.30 g/cc | 0.0470 lb/in3 | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.50 % @Temperature 23.0 °C | 0.50 % @Temperature 73.4 °F | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm @Thickness 3.20 mm | 0.0080 - 0.010 in/in @Thickness 0.126 in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Thickness 3.20 mm | 0.0080 - 0.010 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 250 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 |
| 4.0 g/10 min @Load 2.16 kg, Temperature 250 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 482 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 | |
| 4.8 g/10 min @Load 2.16 kg, Temperature 250 °C | 4.8 g/10 min @Load 4.76 lb, Temperature 482 °F | ASTM D 1238 | |
| 7.0 g/10 min @Load 2.16 kg, Temperature 265 °C | 7.0 g/10 min @Load 4.76 lb, Temperature 509 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 | |
| 8.0 g/10 min @Load 2.16 kg, Temperature 265 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D 1238 | |
| 13 g/10 min @Load 5.00 kg, Temperature 250 °C | 13 g/10 min @Load 11.0 lb, Temperature 482 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 | |
| 15 g/10 min @Load 5.00 kg, Temperature 250 °C | 15 g/10 min @Load 11.0 lb, Temperature 482 °F | ISO 1133 | |
| 15.1 g/10 min @Load 5.00 kg, Temperature 250 °C | 15.1 g/10 min @Load 11.0 lb, Temperature 482 °F | ASTM D 1238 | |
| 23 g/10 min @Load 5.00 kg, Temperature 265 °C | 23 g/10 min @Load 11.0 lb, Temperature 509 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 | |
| 26.7 g/10 min @Load 5.00 kg, Temperature 266 °C | 26.7 g/10 min @Load 11.0 lb, Temperature 511 °F | ASTM D 1238 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527 |
| 42.0 MPa | 6090 psi | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 |
| 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Break | 44 % | 44 % | Type I, 50 mm/min; ASTM D 638 |
| 58 % | 58 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 4.1 % | 4.1 % | 50 mm/min; ISO 527 |
| 4.3 % | 4.3 % | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Modulus | 1.96 GPa | 284 ksi | 1 mm/min; ISO 527 |
| 2.15 GPa | 312 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 71.0 MPa | 10300 psi | 2 mm/min; ISO 178 |
| 72.0 MPa | 10400 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 1.86 GPa | 270 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 1.89 GPa | 274 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 4.27 J/cm @Temperature -40.0 °C | 8.00 ft-lb/in @Temperature -40.0 °F | ASTM D 256 |
| 4.50 J/cm @Temperature -30.0 °C | 8.43 ft-lb/in @Temperature -22.0 °F | ASTM D 256 | |
| 6.94 J/cm @Temperature -20.0 °C | 13.0 ft-lb/in @Temperature -4.00 °F | ASTM D 256 | |
| 7.47 J/cm @Temperature 23.0 °C | 14.0 ft-lb/in @Temperature 73.4 °F | ASTM D 256 | |
| Izod Impact, Notched (ISO) | 40.0 kJ/m2 @Temperature -30.0 °C | 19.0 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1A |
| 43.0 kJ/m2 @Temperature -10.0 °C | 20.5 ft-lb/in2 @Temperature 14.0 °F | 80*10*4; ISO 180/1A | |
| 47.0 kJ/m2 @Temperature 0.000 °C | 22.4 ft-lb/in2 @Temperature 32.0 °F | 80*10*4; ISO 180/1A | |
| 53.0 kJ/m2 @Temperature 23.0 °C | 25.2 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 5.30 J/cm2 @Temperature 23.0 °C | 25.2 ft-lb/in2 @Temperature 73.4 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Impact Test | 56.0 J @Temperature -20.0 °C | 41.3 ft-lb @Temperature -4.00 °F | Instrumented Impact, Energy @ peak; ASTM D 3763 |
| 62.0 J @Temperature 23.0 °C | 45.7 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 | |
| 70.0 J @Temperature -30.0 °C | 51.6 ft-lb @Temperature -22.0 °F | Instrumented Impact Energy @ peak; ASTM D 3763 | |
| 74.0 J @Temperature -40.0 °C | 54.6 ft-lb @Temperature -40.0 °F | Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Electrical Properties | Metric | English | Comments |
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten, PLC code 5; ASTM D 495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | PLC code 0; UL 746A |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | PLC code 2; UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | surface, PLC code 0; UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | PLC code 2; UL 746A |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 98.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 54.4 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 98.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 54.4 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 100 μm/m-°C @Temperature -40.0 - 40.0 °C | 55.6 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 100 μm/m-°C @Temperature -40.0 - 40.0 °C | 55.6 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 110 °C @Thickness 3.20 mm | 230 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| 123 °C @Thickness 6.40 mm | 253 °F @Thickness 0.252 in | unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 74.0 °C @Thickness 3.20 mm | 165 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| 95.0 °C @Thickness 6.40 mm | 203 °F @Thickness 0.252 in | unannealed; ASTM D 648 | |
| Vicat Softening Point | 120 °C | 248 °F | Rate B/50; ASTM D 1525 |
| 120 °C | 248 °F | Rate B/50; ISO 306 | |
| 122 °C | 252 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 75.0 °C | 167 °F | UL 746B |
| UL RTI, Mechanical with Impact | 75.0 °C | 167 °F | UL 746B |
| UL RTI, Mechanical without Impact | 75.0 °C | 167 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.47 mm | V-0 @Thickness 0.0579 in | UL 94 by SABIC-IP |
| 5VA @Thickness 2.99 mm | 5VA @Thickness 0.118 in | UL 94 by SABIC-IP | |
| Oxygen Index | 28 % | 28 % | LOI; ISO 4589 |