- 熔體流動速率 [g/10min]: 45.0
- 缺口沖擊強度: 0.8
- 拉伸強度 [MPa]: 108.0
- 彎曲模量 [MPa]: 8.27
- 熱變形溫度 [℃]: 212.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.73 g/cc | 1.73 g/cc | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm | 0.0020 - 0.0030 in/in @Thickness 0.126 in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0060 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 45 g/10 min @Load 5.00 kg, Temperature 266 °C | 45 g/10 min @Load 11.0 lb, Temperature 511 °F | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Break | 3.1 % | 3.1 % | Type I, 5 mm/min; ASTM D 638 |
| Tensile Modulus | 6.20 GPa | 899 ksi | 5 mm/min; ASTM D 638 |
| Flexural Strength | 155 MPa | 22500 psi | brk, 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 8.27 GPa | 1200 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.800 J/cm @Temperature 23.0 °C | 1.50 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 5.34 J/cm @Temperature 23.0 °C | 10.0 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Electrical Properties | Metric | English | Comments |
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten, PLC code 5; ASTM D 495 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | PLC code 3; UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | PLC code 0; UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | surface, PLC code 0; UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | PLC code 4; UL 746A |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 6.40 mm | 414 °F @Thickness 0.252 in | unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 187 °C @Thickness 6.40 mm | 369 °F @Thickness 0.252 in | unannealed; ASTM D 648 |
| UL RTI, Electrical | 130 °C | 266 °F | UL 746B |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | UL 746B |
| UL RTI, Mechanical without Impact | 140 °C | 284 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 0.760 mm | V-0 @Thickness 0.0299 in | UL 94 |
| 5VA @Thickness 2.99 mm | 5VA @Thickness 0.118 in | UL 94 | |