- 密度 [g/cm3]: 1.6
- 缺口沖擊強度: 0.78
- 拉伸強度 [MPa]: 120.0
- 斷裂伸長率 [%]: 185
- 彎曲模量 [MPa]: 9.83
- 熱變形溫度 [℃]: 222.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in3 | ASTM D 792 |
| 1.60 g/cc | 0.0578 lb/in3 | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.070 % | 0.070 % | 23°C / 50% RH; ISO 62 |
| 0.050 % @Time 86400 sec | 0.050 % @Time 24.0 hour | 50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm @Time 86400 sec | 0.0020 - 0.0050 in/in @Time 24.0 hour | ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.020 cm/cm @Time 86400 sec | 0.0090 - 0.020 in/in @Time 24.0 hour | ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 120 MPa | 17400 psi | 5 mm/min; ISO 527 |
| 121 MPa | 17500 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 120 MPa | 17400 psi | 5 mm/min; ISO 527 |
| 121 MPa | 17500 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D 638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D 638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 11.03 GPa | 1600 ksi | 1 mm/min; ISO 527 |
| 16.88 GPa | 2448 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 185 MPa | 26800 psi | brk, 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Yield Strength | 185 MPa | 26800 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 186 MPa | 27000 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 9.83 GPa | 1430 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 9.88 GPa | 1430 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.780 J/cm @Temperature 23.0 °C | 1.46 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 6.20 J/cm @Temperature 23.0 °C | 11.6 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m2 @Temperature 23.0 °C | 3.33 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m2 @Temperature 23.0 °C | 19.0 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C | 432 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 222 °C @Thickness 3.20 mm | 432 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 207 °C @Thickness 3.20 mm | 405 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |