- 熔體流動速率 [g/10min]: 6.0
- 密度 [g/cm3]: 1.2
- 吸水率 [%]: 0.12
- 缺口沖擊強度: 7.5
- 拉伸強度 [MPa]: 55.0
- 斷裂伸長率 [%]: 80.0
- 彎曲模量 [MPa]: 2.00
- 透光率 [%]: 89.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.12 % | 0.12 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0080 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 265 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D1238 |
| Melt Index of Compound | 6.0 g/10 min @Load 2.16 kg, Temperature 265 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| 110 MPa | 16000 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 120 % | 120 % | 50 mm/min; ISO 527 |
| 130 % | 130 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 5.8 % | 5.8 % | 50 mm/min; ISO 527 |
| 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 1.90 GPa | 276 ksi | 1 mm/min; ISO 527 |
| 2.10 GPa | 305 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
| 85.0 MPa | 12300 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.00 GPa | 290 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.05 GPa | 297 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 7.50 J/cm | 14.1 ft-lb/in | ASTM D256 |
| 0.700 J/cm @Temperature -30.0 °C | 1.31 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| Izod Impact, Notched (ISO) | 11.0 kJ/m2 | 5.23 ft-lb/in2 | 80*10*4; ISO 180/1A |
| 7.00 kJ/m2 @Temperature -30.0 °C | 3.33 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.80 J/cm2 | 8.57 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 68.0 J @Temperature 23.0 °C | 50.2 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 69.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 38.3 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 71.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 39.4 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| CTE, linear, Transverse to Flow | 69.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 38.3 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 71.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 39.4 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C | 208 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 98.0 °C @Thickness 3.20 mm | 208 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Vicat Softening Point | 115 °C | 239 °F | Rate B/50; ASTM D1525 |
| 115 °C | 239 °F | Rate B/50; ISO 306 | |
| 115 °C | 239 °F | Rate B/120; ISO 306 | |
| Optical Properties | Metric | English | Comments |
| Haze | <= 2.0 % @Thickness 2.54 mm | <= 2.0 % @Thickness 0.100 in | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | 2.54 mm; ASTM D1003 |