- 熔體流動速率 [g/10min]: 16.1
- 彎曲模量 [MPa]: 1.70
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.61 g/cc | 1.61 g/cc | ISO 1183 | ||
| Water Absorption | <= 0.30 % | <= 0.30 % | 23°C/24h | ||
| Linear Mold Shrinkage | 0.015 - 0.020 cm/cm | 0.015 - 0.020 in/in | |||
| Melt Flow | <= 16.1 g/10 min @Load 1.20 kg, Temperature 280 °C | <= 16.1 g/10 min @Load 2.65 lb, Temperature 536 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 35.0 MPa | 5080 psi | |||
| Elongation at Yield | 2.4 % | 2.4 % | |||
| 3.0 % | 3.0 % | flexural | |||
| Modulus of Elasticity | 2.00 GPa | 290 ksi | |||
| Flexural Strength | 55.0 MPa | 7980 psi | |||
| Flexural Modulus | 1.70 GPa | 247 ksi | |||
| Charpy Impact Unnotched | 1.50 J/cm2 | 7.14 ft-lb/in2 | edgewise; ISO 179 1eU | ||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |||
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 100 °C | 212 °F | |||
| 180 °C | 356 °F | short term | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 280 °C | 536 °F | mass temp | ||
| Nozzle Temperature | 265 - 275 °C | 509 - 527 °F | |||
| Zone 1 | 285 - 295 °C | 545 - 563 °F | |||
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |||
| Zone 3 | 265 - 275 °C | 509 - 527 °F | |||
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | |||
| Drying Temperature | 80.0 °C @Time 21600 - 28800 sec | 176 °F @Time 6.00 - 8.00 hour | |||
| 120 °C @Time 7200 - 18000 sec | 248 °F @Time 2.00 - 5.00 hour | Dehumidifying dryer | |||
| Descriptive Properties | |||||
| Color | natural color (white) | ||||