- 熔體流動速率 [g/10min]: 15.0
- 缺口沖擊強度: 8.01
- 拉伸強度 [MPa]: 55.17
- 彎曲模量 [MPa]: 2.2069
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Thickness 3.17 mm | 0.0080 in/in @Thickness 0.125 in | 1/8" Section |
| Melt Flow | 15 g/10 min @Load 5.00 kg, Temperature 260 °C | 15 g/10 min @Load 11.0 lb, Temperature 500 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 55.17 MPa | 8002 psi | ASTM D638 |
| Elongation at Break | >= 118 % | >= 118 % | ASTM D638 |
| Flexural Strength | 84.83 MPa | 12300 psi | ASTM D790 |
| Flexural Modulus | 2.2069 GPa | 320.08 ksi | ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm @Thickness 3.17 mm, Temperature 22.8 °C | 15.0 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 121.11 °C | 250.00 °F | ASTM D648 |