- 拉伸強度 [MPa]: 31.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.00 g/cc | 1.00 g/cc | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 27.0 MPa | 3920 psi | ISO 527 | ||
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | ISO 527 | ||
| Elongation at Break | 24 % | 24 % | ISO 527 | ||
| Elongation at Yield | 19 % | 19 % | ISO 527 | ||
| Modulus of Elasticity | 1.90 GPa | 276 ksi | ISO 527 | ||
| Charpy Impact, Notched | 5.10 J/cm2 | 24.3 ft-lb/in2 | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 100 °C | 212 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | ISO 75 | ||
| Vicat Softening Point | 116 °C | 241 °F | VST/B/50; ISO 306 | ||
| Flammability, UL94 | HB | HB | |||
| Descriptive Properties | |||||
| Acid Resistance | yes | ||||
| Aromatic Resistance | no | ||||
| Bondability | yes | ||||
| CKW Resistance | limited | ||||
| Color | Light Grey | ||||
| Hydrocarbonate Resistance | yes | ||||
| Hydroxide Resistance | limited | ||||
| Ketone Resistance | no | ||||
| Physiological indifference according | no | ||||
| Resistance Against Hot Water | no | ||||
| UV Stabilization | limited | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.