- 成型收縮率 [%]: 0.001
- 缺口沖擊強度: 0.883
- 彎曲模量 [MPa]: 9.81
- 熱變形溫度 [℃]: 247.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.68 g/cc | 1.68 g/cc | ASTM D792 | ||
| Moisture Absorption | 0.0500 % @Time 86400 sec | 0.0500 % @Time 24.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 1.60 mm | 0.0010 - 0.0030 in/in @Thickness 0.0630 in | horizontal; ASTM D955 | ||
| 0.0050 - 0.010 cm/cm @Thickness 1.60 mm | 0.0050 - 0.010 in/in @Thickness 0.0630 in | vertical; ASTM D955 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 113 MPa | 16400 psi | ASTM D638 | ||
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 | ||
| Flexural Strength | 175 MPa | 25400 psi | ASTM D790 | ||
| Flexural Modulus | 9.81 GPa | 1420 ksi | ASTM D790 | ||
| Izod Impact, Notched | >= 0.883 J/cm @Thickness 6.35 mm | >= 1.65 ft-lb/in @Thickness 0.250 in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | ASTM D257 | ||
| Dielectric Constant | 3.8 @Frequency 60.0 Hz | 3.8 @Frequency 60.0 Hz | ASTM D150 | ||
| Dielectric Strength | 23.0 kV/mm @Thickness 2.00 mm | 584 kV/in @Thickness 0.0787 in | ASTM D149 | ||
| Dissipation Factor | 0.011 @Frequency 60.0 Hz | 0.011 @Frequency 60.0 Hz | ASTM D150 | ||
| Arc Resistance | 100 sec | 100 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 20.0 μm/m-°C | 11.1 μin/in-°F | ASTM D696 | ||
| Melting Point | 254 °C | 489 °F | DSC | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 247 °C | 477 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ASTM D648 | ||
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 250 - 270 °C | 482 - 518 °F | |||
| Nozzle Temperature | 260 - 280 °C | 500 - 536 °F | |||
| Mold Temperature | 80.0 - 140 °C | 176 - 284 °F | suitable temperature 90-120°C | ||
| Injection Pressure | 50.0 - 120 MPa | 7250 - 17400 psi | |||
| Hold Pressure | 30.0 - 80.0 MPa | 4350 - 11600 psi | |||
| Back Pressure | 0.000 - 0.300 MPa | 0.000 - 43.5 psi | |||
| Screw Speed | 100 - 200 rpm | 100 - 200 rpm | to be chosen in such a way that plasticizing time is just within cooling time | ||
| Descriptive Properties | |||||
| Injection Rate | middle-fast | ||||