- 密度 [g/cm3]: 1.44
- 缺口沖擊強(qiáng)度: 5.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in3 | ISO 1183 | ||
| Moisture Absorption | 0.200 % @Temperature 23.0 °C | 0.200 % @Temperature 73.4 °F | 50% RH; ISO 960 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | Eurotec | ||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | Eurotec | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 115 MPa | 16700 psi | ISO 527 | ||
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 | ||
| Tensile Modulus | 7.00 GPa | 1020 ksi | ISO 527 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 @Temperature -30.0 °C | 2.38 ft-lb/in2 @Temperature -22.0 °F | ISO 180/1A | ||
| 6.00 kJ/m2 @Temperature 23.0 °C | 2.86 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Comparative Tracking Index | 250 V | 250 V | Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 225 °C | 437 °F | [10 K/min], ISO 11357 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 270 - 290 °C | 518 - 554 °F | |||
| Feed Temperature | 50.0 - 70.0 °C | 122 - 158 °F | Throat | ||
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |||
| Drying Temperature | 120 - 140 °C | 248 - 284 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | <= 0.080 % | <= 0.080 % | ISO 960 | ||
| Hold Pressure | 60.0 - 100 MPa | 8700 - 14500 psi | |||
| Descriptive Properties | |||||
| Back Pressure | Low | ||||
| Injection Speed | Fast | ||||