- 密度 [g/cm3]: 1.73
- 缺口沖擊強(qiáng)度: 10.0
- 熱變形溫度 [℃]: 210.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.73 g/cc | 0.0625 lb/in3 | ISO 1183 | ||
| Moisture Absorption | 0.100 % @Temperature 23.0 °C | 0.100 % @Temperature 73.4 °F | 50% RH; ISO 960 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527 | ||
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 | ||
| Tensile Modulus | 17.0 GPa | 2470 ksi | ISO 527 | ||
| Izod Impact, Notched (ISO) | 10.0 kJ/m2 @Temperature -30.0 °C | 4.76 ft-lb/in2 @Temperature -22.0 °F | ISO 180/1A | ||
| 11.0 kJ/m2 @Temperature 23.0 °C | 5.23 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 225 - 255 °C | 437 - 491 °F | [10 K/min], ISO 11357 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 | ||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 260 - 280 °C | 500 - 536 °F | |||
| Feed Temperature | 50.0 - 70.0 °C | 122 - 158 °F | Throat | ||
| Mold Temperature | 60.0 - 110 °C | 140 - 230 °F | |||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |||
| Moisture Content | <= 0.080 % | <= 0.080 % | ISO 960 | ||
| Hold Pressure | 40.0 - 80.0 MPa | 5800 - 11600 psi | |||
| Descriptive Properties | |||||
| Back Pressure | Low | ||||
| Injection Speed | Fast | ||||