- 密度 [g/cm3]: 1.32
- 拉伸強度 [MPa]: 56.0
- 熱變形溫度 [℃]: 70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in3 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 3.8 % | 3.8 % | |
| Tensile Modulus | 2.40 GPa | 348 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 0.270 J/cm2 | 1.28 ft-lb/in2 | |
| 0.290 J/cm2 @Temperature -30.0 °C | 1.38 ft-lb/in2 @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 76.0 μm/m-°C @Temperature 20.0 °C | 42.2 μin/in-°F @Temperature 68.0 °F | in flow direction |
| CTE, linear, Transverse to Flow | 71.0 μm/m-°C @Temperature 20.0 °C | 39.4 μin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft2-°F | |
| Melting Point | 244 °C | 471 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | |
| Vicat Softening Point | 74.0 °C | 165 °F | |
| Glass Transition Temp, Tg | 77.0 °C | 171 °F | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |