- 熔體流動速率 [g/10min]: 11.5
- 缺口沖擊強度: 7.102
- 拉伸強度 [MPa]: 58.2
- 彎曲模量 [MPa]: 2.274
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 11.5 g/10 min @Load 3.80 kg, Temperature 230 °C | 11.5 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 58.2 MPa | 8440 psi | chs 2.0 in/min; ASTM D638 |
| Elongation at Yield | 4.5 % | 4.5 % | chs 2.0 in/min; ASTM D638 |
| Flexural Modulus | 2.274 GPa | 329.8 ksi | chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 7.102 J/cm @Thickness 3.17 mm | 13.30 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 119 °C @Load 1.00 kg, Thickness 3.17 mm | 246 °F @Load 2.20 lb, Thickness 0.125 in | ASTM D1527 |