- 熔體流動速率 [g/10min]: 10.0
- 缺口沖擊強度: 1.6
- 拉伸強度 [MPa]: 62.0
- 彎曲模量 [MPa]: 2.76
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 265 °C | 10 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D5630 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | chs 2.0 in/min; ASTM D638 |
| Flexural Modulus | 2.76 GPa | 400 ksi | tangent; chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 3.00 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 |