- 熔體流動速率 [g/10min]: 66.0
- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.5
- 拉伸強度 [MPa]: 55.0
- 熱變形溫度 [℃]: 150.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.50 % | 0.50 % | Test Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; Test Sim. to ISO 62 | ||
| Viscosity Test | 105 cm3/g | 105 cm3/g | Viscosity number; ISO 307, 1157, 1628 | ||
| Melt Flow | 66 g/10 min @Load 2.16 kg, Temperature 260 °C | 66 g/10 min @Load 4.76 lb, Temperature 500 °F | Calculated from MVR using melt density; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527-1/-2 | ||
| Elongation at Break | 20 % | 20 % | Nominal; ISO 527-1/-2 | ||
| Elongation at Yield | 8.0 % | 8.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 2.80 GPa | 406 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 15.0 J/cm2 @Temperature -30.0 °C | 71.4 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | ||
| 18.0 J/cm2 @Temperature 23.0 °C | 85.7 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | <= 1.00 J/cm2 @Temperature -30.0 °C | <= 4.76 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| <= 1.00 J/cm2 @Temperature 23.0 °C | <= 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Impact | 3944 | 3944 | Puncture maximum force (N); ISO 6603-2 | ||
| 2244 @Temperature -30.0 °C | 2244 @Temperature -22.0 °F | Puncture maximum force (N); ISO 6603-2 | |||
| Puncture Energy | 45.0 J | 33.2 ft-lb | ISO 6603-2 | ||
| 5.00 J @Temperature -30.0 °C | 3.69 ft-lb @Temperature -22.0 °F | ISO 6603-2 | |||
| Tensile Creep Modulus, 1 hour | 2400 MPa | 348000 psi | ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 1400 MPa | 203000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz | 3.2 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.4 @Frequency 100 Hz | 3.4 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0015 @Frequency 100 Hz | 0.0015 @Frequency 100 Hz | IEC 60250 | ||
| 0.019 @Frequency 1.00e+6 Hz | 0.019 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 120 μm/m-°C | 66.7 μin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 120 μm/m-°C | 66.7 μin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 45.0 °C | 113 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 180 °C | 356 °F | 50°C/h 50N; ISO 306 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | IEC 60695-11-10 | ||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | |||
| Oxygen Index | 24 % | 24 % | ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 | ||
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 | ||
| Descriptive Properties | |||||
| Additives | Lubricants | ||||
| Release agent | |||||
| Features | Heat stabilized or stable to heat | ||||
| Form | Pellets | ||||
| ISO Shortname | ISO 7792-1-PBT,GHMR,09-030 | ||||