- 熔體流動速率 [g/10min]: 25.0
- 密度 [g/cm3]: 1.53
- 吸水率 [%]: 0.3
- 熱變形溫度 [℃]: 205.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.30 % | 0.30 % | Test Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 23°C/50% R.H.; Test Sim. to ISO 62 | ||
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 260 °C | 25 g/10 min @Load 4.76 lb, Temperature 500 °F | Calculated from MVR using melt density; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1/-2 | ||
| Elongation at Break | 2.5 % | 2.5 % | ISO 527-1/-2 | ||
| Tensile Modulus | 5.70 GPa | 827 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 3.00 J/cm2 @Temperature -30.0 °C | 14.3 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | ||
| 3.00 J/cm2 @Temperature 23.0 °C | 14.3 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | <= 1.00 J/cm2 @Temperature -30.0 °C | <= 4.76 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| <= 1.00 J/cm2 @Temperature 23.0 °C | <= 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 5500 MPa | 798000 psi | ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 5000 MPa | 725000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz | 3.4 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.6 @Frequency 100 Hz | 3.6 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0040 @Frequency 100 Hz | 0.0040 @Frequency 100 Hz | IEC 60250 | ||
| 0.019 @Frequency 1.00e+6 Hz | 0.019 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 40.0 μm/m-°C | 22.2 μin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 100 μm/m-°C | 55.6 μin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 70.0 °C | 158 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 205 °C | 401 °F | 50°C/h 50N; ISO 306 | ||
| Flammability, UL94 | V-2 @Thickness 0.800 mm | V-2 @Thickness 0.0315 in | IEC 60695-11-10 | ||
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | IEC 60695-11-10 | |||
| 5VA @Thickness 3.50 mm | 5VA @Thickness 0.138 in | IEC 60695-11-20 | |||
| Oxygen Index | 32 % | 32 % | ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 | ||
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 | ||
| Descriptive Properties | |||||
| Features | Flame retardant | ||||
| Form | Pellets | ||||
| ISO Shortname | ISO 7792-1-PBT,GFHMR,09-060,GF12; ISO 1043-PBT GF FR(17) | ||||
| Processing | Injection molding | ||||
| Region | Asia Pacific | ||||
| Europe | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||