Lanxess Pocan? DP T 7140 LDS 000000 PET + PBT, 42% Glass Fiber/Mineral

Lanxess Pocan? DP T 7140 LDS 000000 PET + PBT, 42% Glass Fiber/Mineral 物性表: Lanxess Pocan? DP T 7140 LDS 000000 PET + PBT, 42% Glass Fiber/Mineral物性表及特性介紹,Lanxess Pocan? DP T 7140 LDS 000000 PET + PBT, 42% Glass Fiber/Mineral注塑參數(shù)詳情,如需Lanxess Pocan? DP T 7140 LDS 000000 PET + PBT, 42% Glass Fiber/Mineral下載, 可到相關(guān)下載區(qū)下載

熔體流動速率 [g/10min]: 21.0
缺口沖擊強(qiáng)度: 10.0
彎曲模量 [MPa]: 12.8
熱變形溫度 [℃]: 250.0

Physical Properties	Metric	English	Comments

Specific Gravity	1.74 g/cc	1.74 g/cc	ISO 1183
Bulk Density	1.00 g/cc	0.0361 lb/in3	ISO 60
Viscosity Test	50 cm3/g	50 cm3/g	Viscosity number; ISO 1628-5
Linear Mold Shrinkage, Flow	0.0010 cm/cm	0.0010 in/in	Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
	0.0020 cm/cm	0.0020 in/in	60x60x2; 280°C / WZ 110°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse	0.0020 cm/cm	0.0020 in/in	Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
	0.0070 cm/cm	0.0070 in/in	60x60x2; 280°C / WZ 110°C; 600 bar; ISO 294-4
Melt Flow	21 g/10 min @Load 2.16 kg, Temperature 280 °C	21 g/10 min @Load 4.76 lb, Temperature 536 °F	ISO 1133-1

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	110 MPa	16000 psi	ISO 527-1, -2; 5 mm/min
Elongation at Break	1.3 %	1.3 %	ISO 527-1, -2; 5 mm/min
Tensile Modulus	12.7 GPa	1840 ksi	ISO 527-1, -2; 1 mm/min
Flexural Strength	170 MPa @Strain 1.70 %	24700 psi @Strain 1.70 %	2 mm/min; ISO 178-A
Flexural Modulus	12.8 GPa	1860 ksi	2 mm/min; ISO 178-A
Izod Impact, Notched (ISO)	<= 10.0 kJ/m2 @Temperature 23.0 °C	<= 4.76 ft-lb/in2 @Temperature 73.4 °F	ISO 180-1A
	<= 10.0 kJ/m2 @Temperature -30.0 °C	<= 4.76 ft-lb/in2 @Temperature -22.0 °F	ISO 180-1A
Izod Impact, Unnotched (ISO)	25.0 kJ/m2 @Temperature 23.0 °C	11.9 ft-lb/in2 @Temperature 73.4 °F	ISO 180-1U
	25.0 kJ/m2 @Temperature -30.0 °C	11.9 ft-lb/in2 @Temperature -22.0 °F	ISO 180-1U
Charpy Impact Unnotched	2.50 J/cm2 @Temperature -30.0 °C	11.9 ft-lb/in2 @Temperature -22.0 °F	ISO 179-1eU
	3.00 J/cm2 @Temperature 23.0 °C	14.3 ft-lb/in2 @Temperature 73.4 °F	ISO 179-1eU
Charpy Impact, Notched	<= 1.00 J/cm2 @Temperature 23.0 °C	<= 4.76 ft-lb/in2 @Temperature 73.4 °F	ISO 179-1eA
	<= 1.00 J/cm2 @Temperature -30.0 °C	<= 4.76 ft-lb/in2 @Temperature -22.0 °F	ISO 179-1eA

Electrical Properties	Metric	English	Comments
Volume Resistivity	2.00e+20 ohm-cm	2.00e+20 ohm-cm	IEC 60093
Surface Resistance	5.40e+16 ohm	5.40e+16 ohm	IEC 60093
Dielectric Constant	4.1 @Frequency 1.00e+6 Hz	4.1 @Frequency 1.00e+6 Hz	IEC 60250
	4.3 @Frequency 100 Hz	4.3 @Frequency 100 Hz	IEC 60250
Dielectric Strength	33.0 kV/mm @Thickness 1.00 mm	838 kV/in @Thickness 0.0394 in	IEC 60243-1
Dissipation Factor	0.0022 @Frequency 100 Hz	0.0022 @Frequency 100 Hz	IEC 60250
	0.0138 @Frequency 1.00e+6 Hz	0.0138 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	275 V	275 V	d.a.m.; Solution A; IEC 60112

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	20.0 μm/m-°C @Temperature 23.0 - 55.0 °C	11.1 μin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1, -2
CTE, linear, Transverse to Flow	50.0 μm/m-°C @Temperature 23.0 - 55.0 °C	27.8 μin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1, -2
Thermal Conductivity	0.300 W/m-K	2.08 BTU-in/hr-ft2-°F	ISO 8302
Melting Point	255 °C	491 °F	10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi)	250 °C	482 °F	ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi)	210 °C	410 °F	ISO 75-1, -2
Vicat Softening Point	225 °C @Load 5.10 kg	437 °F @Load 11.2 lb	120°C/hour; ISO 306
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in

Processing Properties	Metric	English	Comments
Melt Temperature	270 - 290 °C	518 - 554 °F
	280 °C	536 °F	for test specimens; ISO 294
Mold Temperature	110 °C	230 °F	for test specimens; ISO 294
	100 - 130 °C	212 - 266 °F
Drying Temperature	120 °C	248 °F
Dry Time	4 - 8 hour	4 - 8 hour
Moisture Content	0.00 - 0.020 %	0.00 - 0.020 %	residual; Karl Fischer Test

Descriptive Properties
ISO Shortname	ISO 7792-1-PET+PBT, GHMR, 07-120, (GF+MD)44

關(guān)鍵詞:
PBT
供應(yīng)
Lanxess Pocan? DP T 7140 LDS 000000 PET + PBT
42% Glass Fiber/Mineral

轉(zhuǎn)載請注明: 轉(zhuǎn)自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/yuanliaoku/show-38691.html

免責(zé)聲明: 本文 Lanxess Pocan? DP T 7140 LDS 000000 PET + PBT, 42% Glass Fiber/Mineral 僅代表作者個人觀點，中國塑膠原料之家無關(guān)。中國塑膠原料之家網(wǎng)所轉(zhuǎn)載的內(nèi)容，其版權(quán)均由原作者和資料提供方所擁有！如因作品版權(quán)問題需要處理，請與我們聯(lián)絡(luò)