- 缺口沖擊強度: 0.58
- 彎曲模量 [MPa]: 5.491
- 硬度: 119.0
- 熱變形溫度 [℃]: 215.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.060 % | 0.060 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.0060 - 0.014 cm/cm | 0.0060 - 0.014 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength | 93.0 MPa | 13500 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Flexural Strength | 167 MPa | 24200 psi | ASTM D790 |
| Flexural Modulus | 5.491 GPa | 796.4 ksi | ASTM D790 |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.5 | 3.5 | ASTM D150 |
| Dielectric Strength | 26.0 kV/mm | 660 kV/in | ASTM D149 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 40.0 μm/m-°C | 22.2 μin/in-°F | ASTM D696 |
| Melting Point | 224 °C | 435 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 178 °C | 352 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |