- 密度 [g/cm3]: 1.54
- 吸水率 [%]: 0.08
- 缺口沖擊強度: 0.5
- 彎曲模量 [MPa]: 5.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in3 | ASTM D792 |
| Water Absorption | 0.080 % | 0.080 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0090 cm/cm | 0.0050 - 0.0090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 88.0 MPa | 12800 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 140 MPa | 20300 psi | ASTM D790 |
| Flexural Modulus | 5.00 GPa | 725 ksi | ASTM D790 |
| Izod Impact, Notched | 0.500 J/cm @Thickness 3.20 mm | 0.937 ft-lb/in @Thickness 0.126 in | ASTM D256 |
| Charpy Impact Unnotched | 3.50 J/cm2 | 16.7 ft-lb/in2 | ISO179 |
| Charpy Impact, Notched | 0.700 J/cm2 | 3.33 ft-lb/in2 | ISO179 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 1e+6 Hz | 3.3 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 20.0 kV/mm @Thickness 2.00 mm | 508 kV/in @Thickness 0.0787 in | ASTM D149 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 38.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 21.1 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | |