- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 0.3
- 彎曲模量 [MPa]: 2.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in3 | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.014 - 0.020 cm/cm | 0.014 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ASTM D638 |
| Flexural Strength | 85.0 MPa | 12300 psi | ASTM D790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM D790 |
| Izod Impact, Notched | 0.300 J/cm @Thickness 3.20 mm | 0.562 ft-lb/in @Thickness 0.126 in | ASTM D256 |
| Charpy Impact Unnotched | 4.00 J/cm2 | 19.0 ft-lb/in2 | ISO179 |
| Charpy Impact, Notched | 0.400 J/cm2 | 1.90 ft-lb/in2 | ISO179 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz | 3.0 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 19.0 kV/mm @Thickness 2.00 mm | 483 kV/in @Thickness 0.0787 in | ASTM D149 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 80.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 44.4 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 225 - 245 °C | 437 - 473 °F | |
| Nozzle Temperature | 240 °C | 464 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Injection Pressure | 40.0 - 100 MPa | 5800 - 14500 psi | |
| Back Pressure | 4.00 - 15.0 MPa | 580 - 2180 psi | |
| Screw Speed | <= 100 rpm | <= 100 rpm | |