- 熔體流動(dòng)速率 [g/10min]: 23.1
- 密度 [g/cm3]: 1.54
- 吸水率 [%]: 0.45
- 熱變形溫度 [℃]: 200.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in3 | ISO 1183 | ||
| Water Absorption at Saturation | 0.45 % | 0.45 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.017 cm/cm | 0.017 in/in | Pigmentation can change mold shrinkage. | ||
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm | 0.017 in/in | Pigmentation can change mold shrinkage. | ||
| Melt Flow | 23.1 g/10 min @Load 2.16 kg, Temperature 250 °C | 23.1 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 82 | 82 | ISO 868 | ||
| Ball Indentation Hardness | 200 MPa | 29000 psi | H30; ISO 2039-1 | ||
| Tensile Strength at Break | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527-1/2 | ||
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527-1/2 | ||
| Tensile Modulus | 4.00 GPa | 580 ksi | ISO 527-1/2 | ||
| Charpy Impact Unnotched | 2.50 J/cm2 @Temperature -30.0 °C | 11.9 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | ||
| 3.00 J/cm2 @Temperature 23.0 °C | 14.3 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.250 J/cm2 @Temperature -30.0 °C | 1.19 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.250 J/cm2 @Temperature 23.0 °C | 1.19 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 4.1 @Frequency 100 Hz | 4.1 @Frequency 100 Hz | IEC 60250 | ||
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | K20/P50; IEC 60243-1 | ||
| Dissipation Factor | 0.016 @Frequency 100 Hz | 0.016 @Frequency 100 Hz | IEC 60250 | ||
| Comparative Tracking Index | 250 V | 250 V | Test Solution A, 100 drops; IEC 60112 | ||
| 275 V | 275 V | Test Solution A, CTI; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 100 μm/m-°C @Temperature 23.0 - 55.0 °C | 55.6 μin/in-°F @Temperature 73.4 - 131 °F | Longitudinal; ISO 11359 | ||
| CTE, linear, Transverse to Flow | 100 μm/m-°C @Temperature 23.0 - 55.0 °C | 55.6 μin/in-°F @Temperature 73.4 - 131 °F | ISO 11359 | ||
| Melting Point | 221 - 226 °C | 430 - 439 °F | DSC | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ISO 75-1/2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75-1/2 | ||
| Vicat Softening Point | 195 °C | 383 °F | 50N; ISO 306 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||||
| Oxygen Index | 23 % | 23 % | ISO 4589 | ||
| Glow Wire Test | 750 °C @Thickness 2.00 mm | 1380 °F @Thickness 0.0787 in | IEC 60695-2-1/0-3 | ||
| Descriptive Properties | |||||
| Electrolytic Corrosion | A1 Step | IEC 60426 | |||