- 熔體流動速率 [g/10min]: 20.64
- 密度 [g/cm3]: 1.72
- 吸水率 [%]: 0.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.72 g/cc | 0.0621 lb/in3 | ISO 1183 |
| Water Absorption at Saturation | 0.40 % | 0.40 % | ISO 62 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm @Thickness 2.00 mm | 0.0010 - 0.0020 in/in @Thickness 0.0787 in | sheet with film gate at rim, mold temperature 80°C |
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm | 0.014 - 0.016 in/in | |
| Melt Flow | 20.64 g/10 min @Load 2.16 kg, Temperature 250 °C | 20.64 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 84 | 84 | ISO 868 |
| Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527-1/2 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1/2 |
| Tensile Modulus | 11.0 GPa | 1600 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 4.00 J/cm2 @Temperature -30.0 °C | 19.0 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU |
| 4.00 J/cm2 @Temperature 23.0 °C | 19.0 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.800 J/cm2 @Temperature -30.0 °C | 3.81 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA |
| 0.800 J/cm2 @Temperature 23.0 °C | 3.81 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Comparative Tracking Index | 250 V | 250 V | Test Solution A CTI; IEC 60112 |
| 250 V | 250 V | 100 drops value; IEC 60112 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 50.0 μm/m-°C @Temperature 23.0 - 55.0 °C | 27.8 μin/in-°F @Temperature 73.4 - 131 °F | Longitudinal; ISO 11359, DIN 53752 |
| Vicat Softening Point | 213 °C | 415 °F | Method B, 50 N; ISO 306 |
| 220 °C | 428 °F | Method A, 10 N; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | IEC 60695 |
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | IEC 60695 | |