- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 0.06
- 缺口沖擊強度: 0.48
- 彎曲強度 [MPa]: 47.0
- 彎曲模量 [MPa]: 1.93
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in3 | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.022 cm/cm @Thickness 3.17 mm | 0.022 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 47.0 MPa | 6820 psi | ASTM D638 |
| Flexural Modulus | 1.93 GPa | 280 ksi | ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm @Thickness 6.35 mm | 0.899 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 238 - 260 °C | 460 - 500 °F | Stock |
| Mold Temperature | 49.0 - 93.0 °C | 120 - 199 °F | |
| Drying Temperature | 82.0 - 93.0 °C | 180 - 199 °F | |