- 密度 [g/cm3]: 1.54
- 吸水率 [%]: 0.05
- 缺口沖擊強(qiáng)度: 8.3
- 彎曲強(qiáng)度 [MPa]: 135.0
- 彎曲模量 [MPa]: 9.00
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in3 | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 93 | 93 | ISO 2039-2 |
| Tensile Strength, Ultimate | 135 MPa | 19600 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.30 kJ/m2 | 3.95 ft-lb/in2 | ISO 180/1A |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.8 @Frequency 100 Hz | 3.8 @Frequency 100 Hz | |
| Dielectric Strength | 21.0 kV/mm @Thickness 3.17 mm | 533 kV/in @Thickness 0.125 in | 50% RH; ASTM D149 |
| Dissipation Factor | 0.0020 @Frequency 100 Hz | 0.0020 @Frequency 100 Hz | |
| Comparative Tracking Index | 320 V | 320 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | UL94 |