- 密度 [g/cm3]: 1.37
- 拉伸強度 [MPa]: 30.0
- 彎曲模量 [MPa]: 1.65
- 熱變形溫度 [℃]: 116.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ASTM D792 | ||
| Density | 1.37 g/cc | 0.0495 lb/in3 | ISO 1183 | ||
| Moisture Absorption | 0.200 % | 0.200 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0250 - 0.0280 cm/cm | 0.0250 - 0.0280 in/in | ISO 294-4 | ||
| 0.0250 - 0.0280 cm/cm | 0.0250 - 0.0280 in/in | ASTM D955 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 105 | 105 | ISO 2039-2 | ||
| Tensile Strength at Break | 34.5 MPa | 5000 psi | ASTM D638 | ||
| Tensile Stress | 32.0 MPa @Strain 50.0 % | 4640 psi @Strain 50.0 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | 50mm/min; ISO 527-2/1A | ||
| 34.5 MPa | 5000 psi | ASTM D638 | |||
| Elongation at Break | 50.0 % | 50.0 % | 50mm/min; ISO 527-2/1A | ||
| >= 50.0 % | >= 50.0 % | 50mm/min; ISO 527-2/1A | |||
| 50.0 % @Temperature 22.8 °C | 50.0 % @Temperature 73.0 °F | ASTM D638 | |||
| Elongation at Yield | 4.50 % | 4.50 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 1.70 GPa | 247 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 50.0 MPa | 7250 psi | ISO 178 | ||
| 58.6 MPa | 8500 psi | ASTM D790 | |||
| Flexural Modulus | 1.65 GPa | 239 ksi | ISO 178 | ||
| 1.79 GPa @Temperature 22.8 °C | 260 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | NB | NB | ASTM D256 | ||
| Izod Impact, Notched (ISO) | NB | NB | ISO 180/1A | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 7.50 J/cm2 | 35.7 ft-lb/in2 | ISO 179/1eA | ||
| 1.50 J/cm2 @Temperature -30.0 °C | 7.14 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Dielectric Constant | 3.60 @Frequency 1.00e+6 Hz | 3.60 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.00 @Frequency 100 Hz | 4.00 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.00450 @Frequency 100 Hz | 0.00450 @Frequency 100 Hz | IEC 60250 | ||
| 0.0170 @Frequency 1.00e+6 Hz | 0.0170 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Arc Resistance | 81.0 sec | 81.0 sec | ASTM D495 | ||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 89.0 μm/m-°C | 49.4 μin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 110 μm/m-°C | 61.1 μin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 240 °F | ASTM D648 | ||
| 127 °C | 261 °F | ISO 75-1, -2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ISO 75-1, -2 | ||
| 54.4 °C | 130 °F | ASTM D648 | |||
| Flammability, UL94 | V-0 | V-0 | UL94 | ||
| V-0 @Thickness 0.850 mm | V-0 @Thickness 0.0335 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 96.0 °C | 149 - 205 °F | Cavity temperature | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Middle Barrel Temperature | 235 - 250 °C | 455 - 482 °F | |||
| Front Barrel Temperature | 240 - 255 °C | 464 - 491 °F | |||
| Nozzle Temperature | 250 - 255 °C | 482 - 491 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 255 °C | 464 - 491 °F | |||
| Die Temperature | 240 - 255 °C | 464 - 491 °F | |||
| Melt Temperature | 235 - 255 °C | 455 - 491 °F | |||
| 235 - 255 °C | 455 - 491 °F | ||||
| 260 °C | 500 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 37.8 - 93.3 °C | 100 - 200 °F | |||
| 82.0 °C | 180 °F | Injection molding; ISO 294 | |||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Hold Pressure | 86.0 MPa | 12500 psi | ISO 294 | ||
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | 100° C. | <= 60 h | |||
| Processing conditions | ISO 7792-2 | ||||
| Processing Notes | Fast Injection Speed | ||||
| Screw Speed - Medium | |||||