- 密度 [g/cm3]: 1.5
- 缺口沖擊強度: 0.481
- 彎曲模量 [MPa]: 4.40
- 熱變形溫度 [℃]: 207.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 | ||
| Density | 1.50 g/cc | 0.0542 lb/in3 | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.010 - 0.014 cm/cm | 0.010 - 0.014 in/in | ASTM D955 | ||
| 0.010 - 0.014 cm/cm | 0.010 - 0.014 in/in | ISO 294-4 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 83 | 83 | ISO 2039-2 | ||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 5mm/min; ISO 527-2/1A | ||
| 75.8 MPa @Temperature 22.8 °C | 11000 psi @Temperature 73.0 °F | ASTM D638 | |||
| Tensile Stress | 16.0 MPa @Strain 0.260 %, Temperature 23.0 °C | 2320 psi @Strain 0.260 %, Temperature 73.4 °F | |||
| 28.6 MPa @Strain 0.520 %, Temperature 23.0 °C | 4150 psi @Strain 0.520 %, Temperature 73.4 °F | ||||
| 39.7 MPa @Strain 0.780 %, Temperature 23.0 °C | 5760 psi @Strain 0.780 %, Temperature 73.4 °F | ||||
| 49.3 MPa @Strain 1.04 %, Temperature 23.0 °C | 7150 psi @Strain 1.04 %, Temperature 73.4 °F | ||||
| 57.7 MPa @Strain 1.30 %, Temperature 23.0 °C | 8370 psi @Strain 1.30 %, Temperature 73.4 °F | ||||
| 64.1 MPa @Strain 1.56 %, Temperature 23.0 °C | 9300 psi @Strain 1.56 %, Temperature 73.4 °F | ||||
| 68.4 MPa @Strain 1.82 %, Temperature 23.0 °C | 9920 psi @Strain 1.82 %, Temperature 73.4 °F | ||||
| 71.1 MPa @Strain 2.08 %, Temperature 23.0 °C | 10300 psi @Strain 2.08 %, Temperature 73.4 °F | ||||
| 72.7 MPa @Strain 2.34 %, Temperature 23.0 °C | 10500 psi @Strain 2.34 %, Temperature 73.4 °F | ||||
| 74.3 MPa @Strain 2.60 %, Temperature 23.0 °C | 10800 psi @Strain 2.60 %, Temperature 73.4 °F | ||||
| Elongation at Break | 3.5 % | 3.5 % | 5mm/min; ISO 527-2/1A | ||
| 4.5 % @Temperature 22.8 °C | 4.5 % @Temperature 73.0 °F | ASTM D638 | |||
| Tensile Modulus | 4.70 GPa | 682 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 | ||
| 121 MPa @Temperature 22.8 °C | 17500 psi @Temperature 73.0 °F | ASTM D790 | |||
| Flexural Modulus | 4.40 GPa | 638 ksi | ISO 178 | ||
| 4.48 GPa @Temperature 22.8 °C | 650 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.481 J/cm @Temperature 22.8 °C | 0.900 ft-lb/in @Temperature 73.0 °F | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 5.60 kJ/m2 | 2.66 ft-lb/in2 | ISO 180/1A | ||
| Charpy Impact Unnotched | 2.10 J/cm2 | 9.99 ft-lb/in2 | ISO 179/1eU | ||
| 2.10 J/cm2 @Temperature 30.0 °C | 9.99 ft-lb/in2 @Temperature 86.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.450 J/cm2 | 2.14 ft-lb/in2 | ISO 179/1eA | ||
| 0.450 J/cm2 @Temperature 30.0 °C | 2.14 ft-lb/in2 @Temperature 86.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| 2.00e+16 ohm-cm | 2.00e+16 ohm-cm | ASTM D257 | |||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.0 @Frequency 1000 Hz | 3.0 @Frequency 1000 Hz | ASTM D150 | ||
| 3.2 @Frequency 1.00e+6 Hz | 3.2 @Frequency 1.00e+6 Hz | ASTM D150 | |||
| 3.4 @Frequency 1.00e+6 Hz | 3.4 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| 3.6 @Frequency 100 Hz | 3.6 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 21.3 kV/mm | 540 kV/in | short term; ASTM D149 | ||
| 27.0 kV/mm | 686 kV/in | IEC 60243-1 | |||
| Dissipation Factor | 0.0033 @Frequency 100 Hz | 0.0033 @Frequency 100 Hz | IEC 60250 | ||
| 0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | ASTM D150 | |||
| 0.0165 @Frequency 1.00e+6 Hz | 0.0165 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Arc Resistance | 78 sec | 78 sec | ASTM D495 | ||
| Comparative Tracking Index | 225 V | 225 V | IEC 60112 | ||
| 250 V | 250 V | ASTM D3638 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 60.0 μm/m-°C | 33.3 μin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 207 °C | 405 °F | ASTM D648 | ||
| 210 °C | 410 °F | ISO 75-1, -2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ISO 75-1, -2 | ||
| 157 °C | 315 °F | ASTM D648 | |||
| Deflection Temperature at 8.0 MPa | 55.0 °C | 131 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 200 °C | 392 °F | B50 (50°C/h 50N); ISO 306 | ||
| Glass Transition Temp, Tg | 60.0 °C | 140 °F | ISO 11357-1,-2,-3 | ||
| Flammability, UL94 | V-0 | V-0 | |||
| V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | ||||
| 5VA @Thickness 3.00 mm | 5VA @Thickness 0.118 in | ||||
| Oxygen Index | 30 % | 30 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper | ||
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 255 °C | 464 - 491 °F | |||
| Die Temperature | 250 - 255 °C | 482 - 491 °F | |||
| Melt Temperature | 235 - 255 °C | 455 - 491 °F | |||
| 260 °C | 500 °F | ISO 294 | |||
| Mold Temperature | 82.0 °C | 180 °F | ISO 294 | ||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.020 % | 0.020 % | Necessary low maximum | ||
| Injection Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Melt volume rate (MVR), cm3/10min | 13 | ||||
| MVR test load, kg | 2.16 | ||||
| MVR test temperature, °C | 250 | ||||
| Processing conditions acc. ISO | 7792-2 | ||||