- 熔體流動速率 [g/10min]: 35.0
- 密度 [g/cm3]: 1.31
- 缺口沖擊強度: 0.374
- 拉伸強度 [MPa]: 60.0
- 彎曲模量 [MPa]: 2.55
- 熱變形溫度 [℃]: 150.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 | ||
| Density | 1.31 g/cc | 0.0473 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | ASTM D955 | ||
| 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | ISO 294-4 | |||
| Melt Flow | 35 g/10 min | 35 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 79 | 79 | ISO 2039-2 | ||
| Tensile Stress | 9.44 MPa @Strain 0.370 %, Temperature 23.0 °C | 1370 psi @Strain 0.370 %, Temperature 73.4 °F | |||
| 18.63 MPa @Strain 0.730 %, Temperature 23.0 °C | 2702 psi @Strain 0.730 %, Temperature 73.4 °F | ||||
| 27.42 MPa @Strain 1.10 %, Temperature 23.0 °C | 3977 psi @Strain 1.10 %, Temperature 73.4 °F | ||||
| 35.54 MPa @Strain 1.46 %, Temperature 23.0 °C | 5155 psi @Strain 1.46 %, Temperature 73.4 °F | ||||
| 42.87 MPa @Strain 1.83 %, Temperature 23.0 °C | 6218 psi @Strain 1.83 %, Temperature 73.4 °F | ||||
| 49.22 MPa @Strain 2.19 %, Temperature 23.0 °C | 7139 psi @Strain 2.19 %, Temperature 73.4 °F | ||||
| 54.19 MPa @Strain 2.56 %, Temperature 23.0 °C | 7860 psi @Strain 2.56 %, Temperature 73.4 °F | ||||
| 57.33 MPa @Strain 2.92 %, Temperature 23.0 °C | 8315 psi @Strain 2.92 %, Temperature 73.4 °F | ||||
| 58.65 MPa @Strain 3.29 %, Temperature 23.0 °C | 8506 psi @Strain 3.29 %, Temperature 73.4 °F | ||||
| 58.93 MPa @Strain 3.65 %, Temperature 23.0 °C | 8547 psi @Strain 3.65 %, Temperature 73.4 °F | ||||
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50mm/min; ISO 527-2/1A | ||
| 55.8 MPa @Temperature 22.8 °C | 8100 psi @Temperature 73.0 °F | ASTM D638 | |||
| Elongation at Break | 40 % | 40 % | 50mm/min; ISO 527-2/1A | ||
| 60 % @Temperature 22.8 °C | 60 % @Temperature 73.0 °F | ASTM D638 | |||
| Elongation at Yield | 4.0 % | 4.0 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 2.70 GPa | 392 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 | ||
| 82.7 MPa @Temperature 22.8 °C | 12000 psi @Temperature 73.0 °F | ASTM D790 | |||
| Flexural Modulus | 2.55 GPa | 370 ksi | ISO 178 | ||
| 2.41 GPa @Temperature 22.8 °C | 350 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.374 J/cm @Temperature 22.8 °C | 0.700 ft-lb/in @Temperature 73.0 °F | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 4.00 kJ/m2 | 1.90 ft-lb/in2 | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 63.0 kJ/m2 @Temperature 23.0 °C | 30.0 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1U | ||
| Charpy Impact Unnotched | 20.5 J/cm2 | 97.5 ft-lb/in2 | ISO 179/1eU | ||
| 5.80 J/cm2 @Temperature 30.0 °C | 27.6 ft-lb/in2 @Temperature 86.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.430 J/cm2 | 2.05 ft-lb/in2 | ISO 179/1eA | ||
| 0.430 J/cm2 @Temperature 30.0 °C | 2.05 ft-lb/in2 @Temperature 86.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | |||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz | 3.2 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 3.2 @Frequency 1.00e+6 Hz | 3.2 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| 4.1 @Frequency 100 Hz | 4.1 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0020 @Frequency 1.00e+6 Hz | 0.0020 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 110 μm/m-°C | 61.1 μin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ISO 75-1, -2 | ||
| 157 °C | 315 °F | ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.2 °C | 126 °F | ASTM D648 | ||
| 55.0 °C | 131 °F | ISO 75-1, -2 | |||
| Vicat Softening Point | 190 °C | 374 °F | B50 (50°C/h 50N); ISO 306 | ||
| Glass Transition Temp, Tg | 60.0 °C | 140 °F | ISO 11357-1,-2,-3 | ||
| Flammability, UL94 | HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | |||
| Oxygen Index | 22 % | 22 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper | ||
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 243 °C | 469 °F | ISO 294 | ||
| 235 - 260 °C | 455 - 500 °F | ||||
| Mold Temperature | 48.0 °C | 118 °F | ISO 294 | ||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.020 % | 0.020 % | Necessary low maximum | ||
| Injection Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Melt volume rate (MVR), cm3/10min | 44 | ||||
| MVR test load, kg | 2.16 | ||||
| MVR test temperature, °C | 250 | ||||
| Processing conditions acc. ISO | 7792-2 | ||||