- 密度 [g/cm3]: 1.47
- 彎曲模量 [MPa]: 27.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in3 | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 220 MPa | 31900 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 0.850 % | 0.850 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 32.0 GPa | 4640 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 375 MPa | 54400 psi | ISO 178 | ||
| Flexural Modulus | 27.5 GPa | 3990 ksi | ISO 178 | ||
| Charpy Impact, Notched | 1.60 J/cm2 | 7.61 ft-lb/in2 | ISO 179/1eA | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Dew Point | <= -30.0 °C | <= -22.0 °F | Pre-drying | ||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||