- 密度 [g/cm3]: 1.66
- 缺口沖擊強度: 0.694
- 彎曲模量 [MPa]: 12.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00100 cm/cm | 0.00100 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00500 cm/cm | 0.00500 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 147 MPa | 21300 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 2.10 % | 2.10 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 13.5 GPa | 1960 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
| Flexural Modulus | 12.5 GPa | 1810 ksi | ISO 178 |
| Izod Impact, Notched | 0.694 J/cm | 1.30 ft-lb/in | ASTM D256 |
| 0.854 J/cm @Temperature -30.0 °C | 1.60 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| Charpy Impact, Notched | 0.750 J/cm2 | 3.57 ft-lb/in2 | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1, -2 |