- 熔體流動(dòng)速率 [g/10min]: 10.0
- 密度 [g/cm3]: 1.5
- 吸水率 [%]: 0.1
- 缺口沖擊強(qiáng)度: 1.07
- 彎曲模量 [MPa]: 8.50
- 熱變形溫度 [℃]: 210.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 | ||
| Density | 1.50 g/cc | 0.0542 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.100 % | 0.100 % | 24hr immersion; ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.00400 - 0.00600 cm/cm | 0.00400 - 0.00600 in/in | ASTM D955 | ||
| 0.00400 - 0.00600 cm/cm | 0.00400 - 0.00600 in/in | ISO 294-4 | |||
| Melt Flow | 10.0 g/10 min | 10.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 73.0 | 73.0 | ISO 2039-2 | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | 5mm/min; ISO 527-2/1A | ||
| 121 MPa | 17500 psi | ASTM D638 | |||
| Elongation at Break | 2.90 % | 2.90 % | 5mm/min; ISO 527-2/1A | ||
| 3.00 % @Temperature 22.8 °C | 3.00 % @Temperature 73.0 °F | ASTM D638 | |||
| Tensile Modulus | 9.20 GPa | 1330 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 179 MPa | 26000 psi | ASTM D790 | ||
| 180 MPa | 26100 psi | ISO 178 | |||
| Flexural Modulus | 8.50 GPa | 1230 ksi | ISO 178 | ||
| 8.27 GPa @Temperature 22.8 °C | 1200 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 12.0 kJ/m2 | 5.71 ft-lb/in2 | ISO 180/1A | ||
| Charpy Impact Unnotched | 6.00 J/cm2 | 28.6 ft-lb/in2 | ISO 179/1eU | ||
| 4.50 J/cm2 @Temperature -30.0 °C | 21.4 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.19 J/cm2 | 5.66 ft-lb/in2 | ISO 179/1eA | ||
| 1.10 J/cm2 @Temperature -30.0 °C | 5.23 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 19.3 kV/mm | 490 kV/in | short term; ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 20.0 μm/m-°C | 11.1 μin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 87.0 μm/m-°C | 48.3 μin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1, -2 | ||
| 223 °C | 433 °F | ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 164 °C | 327 °F | ISO 75-1, -2 | ||
| 209 °C | 408 °F | ASTM D648 | |||
| Flammability, UL94 | HB | HB | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 93.0 °C | 149 - 199 °F | Cavity temperature | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Middle Barrel Temperature | 235 - 250 °C | 455 - 482 °F | |||
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| 235 - 260 °C | 455 - 500 °F | ||||
| 260 °C | 500 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |||
| 82.0 °C | 180 °F | Injection molding; ISO 294 | |||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Hold Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | lower the temperature to 100° C until processed. | <= 60 h | |||
| Processing conditions | ISO 7792-2 | ||||
| Processing Notes | Fast Injection Speed | ||||
| Medium Screw Speed | |||||