- 密度 [g/cm3]: 1.49
- 缺口沖擊強度: 13.9
- 彎曲模量 [MPa]: 8.70
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.00300 - 0.00500 cm/cm | 0.00300 - 0.00500 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 2.80 % | 2.80 % | 5mm/min; ISO 527-2/1A | ||
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 | ||
| Flexural Modulus | 8.70 GPa | 1260 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 13.9 kJ/m2 | 6.61 ft-lb/in2 | ISO 180/1A | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 173 °C | 343 °F | ISO 75-1, -2 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 96.0 °C | 149 - 205 °F | Cavity temperature | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Middle Barrel Temperature | 235 - 250 °C | 455 - 482 °F | |||
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| 235 - 260 °C | 455 - 500 °F | ||||
| 260 °C | 500 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |||
| 82.0 °C | 180 °F | Injection molding; ISO 294 | |||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Hold Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | lower the temperature to 100° C until processed. | <= 60 h | |||
| Processing conditions | ISO 7792-2 | ||||
| Processing Notes | Fast Injection Speed | ||||
| Medium Screw Speed | |||||