- 熔體流動速率 [g/10min]: 2.2
- 密度 [g/cm3]: 1.2
- 缺口沖擊強度: 40.0
- 拉伸強度 [MPa]: 33.0
- 熱變形溫度 [℃]: 83.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in3 | |
| Melt Flow | 2.2 g/10 min @Load 2.16 kg, Temperature 250 °C | 2.2 g/10 min @Load 4.76 lb, Temperature 482 °F | cm3/10 min |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal strain at break (50 mm/min) |
| Elongation at Yield | 4.6 % | 4.6 % | 50 mm/min |
| Tensile Modulus | 1.40 GPa | 203 ksi | 1 mm/min |
| Izod Impact, Unnotched | NB | NB | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ||
| Izod Impact, Notched (ISO) | 40.0 kJ/m2 @Temperature -30.0 °C | 19.0 ft-lb/in2 @Temperature -22.0 °F | |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 83.0 °C | 181 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.0 °C | 124 °F | |
| Vicat Softening Point | 105 °C | 221 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |