- 密度 [g/cm3]: 1.58
- 熱變形溫度 [℃]: 218.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in3 | ISO 1183 | ||
| Filler Content | 15 % | 15 % | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 100 MPa @Temperature 23.0 °C | 14500 psi @Temperature 73.4 °F | ISO 527 | ||
| Elongation at Break | 3.4 % @Temperature 23.0 °C | 3.4 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 7.20 GPa @Temperature 23.0 °C | 1040 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 155 MPa @Temperature 23.0 °C | 22500 psi @Temperature 73.4 °F | ISO 178 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 116 °C | 241 °F | ISO 75-1/-2 | ||
| UL RTI, Electrical | 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | UL 746B | ||
| 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | UL 746B | |||
| UL RTI, Mechanical with Impact | 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL 746B | ||
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | UL 746B | |||
| UL RTI, Mechanical without Impact | 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | UL 746B | ||
| 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | UL 746B | |||
| Flammability, UL94 | V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | UL94 | ||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL94 | |||
| V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | UL94 | |||
| Oxygen Index | 32 % | 32 % | ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| 240 - 260 °C | 464 - 500 °F | ||||
| Mold Temperature | 80.0 °C | 176 °F | optimum | ||
| 30.0 - 130 °C | 86.0 - 266 °F | ||||
| Drying Temperature | 110 - 130 °C | 230 - 266 °F | |||
| Moisture Content | <= 0.040 % | <= 0.040 % | |||
| Descriptive Properties | |||||
| Appearance | Black Color | ||||
| Features | Flame Retardant | ||||
| Filler | Glass Reinforced | ||||
| Forms | Pellets | ||||
| Generic | PBT | ||||
| Material Status | Current | ||||
| Part Marking Code | >PBT-GF15FR(17)< | ISO 11469 | |||
| Processing Method | Injection Molding | ||||
| Product Category | Flame Retardant Resins | ||||
| Glass Reinforced Resins | |||||
| Region Available - Global | Yes | ||||
| Resin Identification | PBT-GF15FR(17) | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||