- 彎曲模量 [MPa]: 6.29
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Flexural Strength | 46.2 MPa | 6700 psi | 5 lb Core, 6 hrs @ 220°F, Vacuum Bag | ||
| 49.0 MPa | 7100 psi | 8 lb Core, 6 hrs @ 220°F, Vacuum Bag | |||
| Flexural Modulus | 6.29 GPa | 913 ksi | 5 lb Core, 6 hrs @ 220°F, Vacuum Bag | ||
| 6.76 GPa | 980 ksi | 8 lb Core, 6 hrs @ 220°F, Vacuum Bag | |||
| Shear Strength | 15.13 MPa @Temperature 82.2 °C | 2195 psi @Temperature 180 °F | Cure Cycle, 2 hrs @ 250°F, FPL Acid Etched 6061-T6, Std Dev 94; ASTM D1002 | ||
| 17.13 MPa @Temperature 82.2 °C | 2485 psi @Temperature 180 °F | Cure Cycle, 4 hrs @ 220°F, FPL Acid Etched 6061-T6, Std Dev 132; ASTM D1002 | |||
| 17.33 MPa @Temperature 82.2 °C | 2513 psi @Temperature 180 °F | Cure Cycle, 8 hrs @ 180°F, FPL Acid Etched 6061-T6, Std Dev 158; ASTM D1002 | |||
| 19.68 MPa @Temperature 60.0 °C | 2855 psi @Temperature 140 °F | Cure Cycle, 2 hrs @ 250°F, FPL Acid Etched 6061-T6, Std Dev 64; ASTM D1002 | |||
| 21.59 MPa @Temperature 60.0 °C | 3131 psi @Temperature 140 °F | Cure Cycle, 4 hrs @ 220°F, FPL Acid Etched 6061-T6, Std Dev 72; ASTM D1002 | |||
| 22.39 MPa @Temperature 60.0 °C | 3248 psi @Temperature 140 °F | Cure Cycle, 8 hrs @ 180°F, FPL Acid Etched 6061-T6, Std Dev 144; ASTM D1002 | |||
| 22.45 MPa @Temperature 21.1 °C | 3256 psi @Temperature 70.0 °F | Cure Cycle, 8 hrs @ 180°F, FPL Acid Etched 6061-T6, Std Dev 502; ASTM D1002 | |||
| 22.5 MPa @Temperature 21.1 °C | 3270 psi @Temperature 70.0 °F | Cure Cycle, 2 hrs @ 250°F, FPL Acid Etched 6061-T6, Std Dev 470; ASTM D1002 | |||
| 23.30 MPa @Temperature 60.0 °C | 3379 psi @Temperature 140 °F | Cure Cycle, 6 hrs @ 200°F, FPL Acid Etched 6061-T6, Std Dev 100; ASTM D1002 | |||
| 24.1 MPa @Temperature 82.2 °C | 3490 psi @Temperature 180 °F | Cure Cycle, 2 hrs @ 250°F, FPL Acid Etched 6061-T6, Std Dev 121; ASTM D1002 | |||
| 24.1 MPa @Temperature 82.2 °C | 3500 psi @Temperature 180 °F | 2 hrs @ 250°F, Metal Clamp Pressure, 6061 T6 FPL Etched | |||
| 24.29 MPa @Temperature 21.1 °C | 3523 psi @Temperature 70.0 °F | Cure Cycle, 1 hr @ 250°F, FPL Acid Etched 6061-T6, Std Dev 456; ASTM D1002 | |||
| 24.51 MPa @Temperature 82.2 °C | 3555 psi @Temperature 180 °F | Cure Cycle, 6 hrs @ 200°F, FPL Acid Etched 6061-T6, Std Dev 150; ASTM D1002 | |||
| 27.10 MPa @Temperature 71.1 °C | 3931 psi @Temperature 160 °F | Cure Cycle, 2 hrs @ 250°F, FPL Acid Etched 6061-T6, Std Dev 138; ASTM D1002 | |||
| 27.6 MPa @Temperature 21.1 °C | 4010 psi @Temperature 70.0 °F | Cure Cycle, 6 hrs @ 200°F, FPL Acid Etched 6061-T6, Std Dev 109; ASTM D1002 | |||
| 27.9 MPa @Temperature 60.0 °C | 4040 psi @Temperature 140 °F | Cure Cycle, 2 hrs @ 250°F, FPL Acid Etched 6061-T6, Std Dev 117; ASTM D1002 | |||
| 27.97 MPa @Temperature 21.1 °C | 4056 psi @Temperature 70.0 °F | Cure Cycle, 2 hrs @ 250°F, FPL Acid Etched 6061-T6, Std Dev 218; ASTM D1002 | |||
| 28.14 MPa @Temperature 21.1 °C | 4082 psi @Temperature 70.0 °F | Cure Cycle, 4 hrs @ 220°F, FPL Acid Etched 6061-T6, Std Dev 128; ASTM D1002 | |||
| 30.74 MPa @Temperature 21.1 °C | 4459 psi @Temperature 70.0 °F | Cure Cycle, 6 hrs @ 220°F, FPL Acid Etched 6061-T6, Std Dev 134; ASTM D1002 | |||
| 32.30 MPa @Temperature 21.1 °C | 4685 psi @Temperature 70.0 °F | Cure Cycle, 1 hr @ 250°F, FPL Acid Etched 6061-T6, Std Dev 9; ASTM D1002 | |||
| 32.55 MPa @Temperature 21.1 °C | 4721 psi @Temperature 70.0 °F | Cure Cycle, 2 hrs @ 250°F, FPL Acid Etched 6061-T6, Std Dev 128; ASTM D1002 | |||
| 32.73 MPa @Temperature 21.1 °C | 4747 psi @Temperature 70.0 °F | Cure Cycle, 90 min @ 250°F, FPL Acid Etched 6061-T6, Std Dev 84; ASTM D1002 | |||
| 34.5 MPa @Temperature 21.1 °C | 5000 psi @Temperature 70.0 °F | 2 hrs @ 250°F, Metal Clamp Pressure, 6061 T6 FPL Etched | |||
| 35.32 MPa @Temperature 21.1 °C | 5123 psi @Temperature 70.0 °F | Cure Cycle, 90 min @ 250°F, FPL Acid Etched 6061-T6, Std Dev 96; ASTM D1002 | |||
| Peel Strength | 5.33 kN/m | 30.4 pli | T-Peel, Cure Cycle, 1 hr @ 250°F, FPL Acid Etched 6061-T6, Std Dev 1.6; ASTM D1876 | ||
| 5.40 kN/m | 30.8 pli | T-Peel, Cure Cycle, 6 hrs @ 220°F, FPL Acid Etched 6061-T6, Std Dev 1.9; ASTM D1876 | |||
| 6.28 kN/m | 35.8 pli | T-Peel, Cure Cycle, 90 min @ 250°F, FPL Acid Etched 6061-T6, Std Dev 2.3; ASTM D1876 | |||
| 6.82 kN/m | 38.9 pli | T-Peel, Cure Cycle, 90 min @ 250°F, FPL Acid Etched 6061-T6, Std Dev 3.1; ASTM D1876 | |||
| 7.10 kN/m | 40.5 pli | T-Peel, Cure Cycle, 2 hrs @ 250°F, FPL Acid Etched 6061-T6, Std Dev 3.4; ASTM D1876 | |||
| 3.51 kN/m @Temperature 82.2 °C | 20.0 pli @Temperature 180 °F | T-Peel, 2 hrs @ 250°F, Metal Clamp Pressure, 6061 T6 FPL Etched | |||
| 7.19 kN/m @Temperature 21.1 °C | 41.0 pli @Temperature 70.0 °F | T-Peel, 2 hrs @ 250°F, Metal Clamp Pressure, 6061 T6 FPL Etched | |||
| Descriptive Properties | |||||
| Drum Peel | 19.8 in-lb/in | Tool Side Up, 2 hrs @ 250°F, 30 psi, 6061 T6 Abraded, 1” Nomex 3 lb core 1/8” cell | |||
| 20.5 in-lb/in | Tool Side Down, 2 hrs @ 250°F, 30 psi, 6061 T6 Abraded, 1” Nomex 3 lb core 1/8” cell | ||||
| Load to Failure | 606 lbf | 5 lb Core, 6 hrs @ 220°F, Vacuum Bag | |||
| 669 lbf | 8 lb Core, 6 hrs @ 220°F, Vacuum Bag | ||||