Zyvex Performance Materials Arovex? HT 250 Nano-Engineered Composite Prepreg System

Zyvex Performance Materials Arovex? HT 250 Nano-Engineered Composite Prepreg System 物性表: Zyvex Performance Materials Arovex? HT 250 Nano-Engineered Composite Prepreg System物性表及特性介紹,Zyvex Performance Materials Arovex? HT 250 Nano-Engineered Composite Prepreg System注塑參數(shù)詳情,如需Zyvex Performance Materials Arovex? HT 250 Nano-Engineered Composite Prepreg System下載, 可到相關(guān)下載區(qū)下載

彎曲模量 [MPa]: 56.0

Physical Properties	Metric	English	Comments

Viscosity	0.0500 cP @Temperature 120 °C	0.0500 cP @Temperature 248 °F	Rheology, 2°C/min
	0.0700 cP @Temperature 80.0 °C	0.0700 cP @Temperature 176 °F	Rheology, 2°C/min
	1.00 cP @Temperature 40.0 °C	1.00 cP @Temperature 104 °F	Rheology, 2°C/min
	100 cP @Temperature 140 °C	100 cP @Temperature 284 °F	Rheology, 2°C/min

Mechanical Properties	Metric	English	Comments
Tensile Strength	758 MPa	110000 psi	with 3K Plain Weave AS-2 Carbon Fiber; ASTM D638
	889 MPa	129000 psi	with 3K Resin with 3K Twill TR30 Carbon Fiber; ASTM D638
Tensile Modulus	64.9 GPa	9410 ksi	with 3K Resin with 3K Twill TR30 Carbon Fiber; ASTM D638
	71.4 GPa	10400 ksi	with 3K Plain Weave AS-2 Carbon Fiber; ASTM D638
Flexural Strength	807 MPa	117000 psi	with 3K Plain Weave AS-2 Carbon Fiber; ASTM D790
	1010 MPa	146000 psi	with 3K Resin with 3K Twill TR30 Carbon Fiber; ASTM D790
Flexural Modulus	56.0 GPa	8120 ksi	with 3K Plain Weave AS-2 Carbon Fiber; ASTM D790
	56.7 GPa	8220 ksi	with 3K Resin with 3K Twill TR30 Carbon Fiber; ASTM D790
Compressive Strength	456 MPa	66100 psi	with 3K Plain Weave AS-2 Carbon Fiber; ASTM D695
	601 MPa	87200 psi	with 3K Resin with 3K Twill TR30 Carbon Fiber; ASTM D695
Shear Strength	71.4 MPa	10400 psi	Short Beam, with 3K Plain Weave AS-2 Carbon Fiber; ASTM D2344
	74.39 MPa	10790 psi	Short Beam, with 3K Resin with 3K Twill TR30 Carbon Fiber; ASTM D2344

Thermal Properties	Metric	English	Comments
Glass Transition Temp, Tg	112.4 °C	234.3 °F	with 3K Resin with 3K Twill TR30 Carbon Fiber; ASTM D7028-07
	125 °C	258 °F	with 3K Plain Weave AS-2 Carbon Fiber; ASTM D7028-07

Processing Properties	Metric	English	Comments
Cure Time	30.0 min @Temperature 137.8 °C	0.500 hour @Temperature 280.0 °F
	120 min @Temperature 121.1 °C	2.00 hour @Temperature 250.0 °F
	120 min @Temperature 121 °C	2.00 hour @Temperature 250 °F	80 psi
	240 min @Temperature 104.4 °C	4.00 hour @Temperature 219.9 °F
	360 min @Temperature 93.3 °C	6.00 hour @Temperature 200 °F
	720 min @Temperature 82.2 °C	12.0 hour @Temperature 180 °F
Gel Time	5.00 min @Temperature 137.8 °C	5.00 min @Temperature 280.0 °F
	13.0 min @Temperature 121.1 °C	13.0 min @Temperature 250.0 °F
	33.0 min @Temperature 104.4 °C	33.0 min @Temperature 219.9 °F
	68.0 min @Temperature 93.3 °C	68.0 min @Temperature 200 °F
	168 min @Temperature 82.2 °C	168 min @Temperature 180 °F
Shelf Life	12.0 Month @Temperature -17.8 °C	12.0 Month @Temperature 0.000 °F

Descriptive Properties
GIC Mode I Energy	4.2 in-lb/in2		ASTM D5528-07, with 3K Twill TR30 Carbon Fiber
	4.8 in-lb/in2		ASTM D5528-07, with 3K Plain Weave AS-2 Carbon Fiber

關(guān)鍵詞:
供應(yīng)
熱固性復(fù)合材料
Zyvex Performance Materials Arovex? HT 250 Nano-Engineered Composite Prepreg System

轉(zhuǎn)載請注明: 轉(zhuǎn)自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/yuanliaoku/show-37709.html

免責聲明: 本文 Zyvex Performance Materials Arovex? HT 250 Nano-Engineered Composite Prepreg System 僅代表作者個人觀點，中國塑膠原料之家無關(guān)。中國塑膠原料之家網(wǎng)所轉(zhuǎn)載的內(nèi)容，其版權(quán)均由原作者和資料提供方所擁有！如因作品版權(quán)問題需要處理，請與我們聯(lián)絡(luò)